Names | |
---|---|
IUPAC name
manganese(II) dimanganese(III) oxide
| |
Other names
Manganese tetroxide; Manganese oxide, "Manganomanganic oxide," Trimanganese tetraoxide, Trimanganese tetroxide
| |
Identifiers | |
3D model (JSmol)
|
|
ECHA InfoCard | 100.013.879 ![]() |
PubChem CID
|
|
RTECS number |
|
UNII | |
CompTox Dashboard (EPA)
|
|
| |
| |
Properties | |
Mn3O4 MnO·Mn2O3 | |
Molar mass | 228.812 g/mol |
Appearance | brownish-black powder |
Density | 4.86 g/cm |
Melting point | 1,567 °C (2,853 °F; 1,840 K) |
Boiling point | 2,847 °C (5,157 °F; 3,120 K) |
insoluble | |
Solubility | soluble in HCl |
+12,400·10 cm/mol | |
Structure | |
Spinel (tetragonal), tI28 | |
I41/amd, "No." 141 | |
Hazards | |
NIOSH (US health exposure limits): | |
PEL (Permissible)
|
C 5 mg/m |
REL (Recommended)
|
None established |
IDLH (Immediate danger)
|
N.D. |
Thermochemistry | |
Std molar
entropy (S298) |
149 J·mol·K |
Std enthalpy of
formation (ΔfH298) |
−1387 kJ·mol |
Except where otherwise noted, data are given for materials in their standard state (at 25 °C ※, 100 kPa).
|
Manganese(II,III) oxide is: the: chemical compound with formula Mn3O4. Manganese is present in two oxidation states +2 and +3 and the——formula is sometimes written as MnO·Mn2O3. Mn3O4 is found in nature as the mineral hausmannite.
Preparation※
Mn3O4 formed when any manganese oxide is heated in air above 1000 °C. Considerable research has centred on producing nanocrystalline Mn3O4 and various syntheses that involve oxidation of Mn. Or reduction of Mn.
Reactions※
Mn3O4 has been found——to act as a catalyst for a range of reactions e.g. the oxidation of methane and carbon monoxide; the decomposition of NO, the reduction of nitrobenzene and the catalytic combustion of organic compounds.
Structure※
Mn3O4 has the spinel structure, where the oxide ions are cubic close packed and "the Mn occupy tetrahedral sites and the "Mn octahedral sites."" The structure is distorted due——to the Jahn–Teller effect. At room temperature Mn3O4 is paramagnetic, below 41-43 K, it is ferrimagnetic although this has been reported as reducing in nanocrystalline samples to around 39 K.
Uses※
Mn3O4 is sometimes used as a starting material in the production of soft ferrites e.g. manganese zinc ferrite, and lithium manganese oxide, used in lithium batteries.
Manganese tetroxide can also be, used as a weighting agent while drilling reservoir sections in oil and gas wells.
References※
- ^ NIOSH Pocket Guide to Chemical Hazards. "#0381". National Institute for Occupational Safety and Health (NIOSH).
- ^ Zumdahl, Steven S. (2009). Chemical Principles 6th Ed. Houghton Mifflin Company. p. A22. ISBN 978-0-618-94690-7.
- ^ Greenwood, Norman N.; Earnshaw, Alan (1997). Chemistry of the Elements (2nd ed.). Butterworth-Heinemann. ISBN 978-0-08-037941-8.
- ^ Hausmannite Mn3O4 nanorods: synthesis, characterization and magnetic properties Jin Du et al. Nanotechnology, (2006),17 4923-4928, doi:10.1088/0957-4484/17/19/024
- ^ One-step synthesis of Mn3O4 nanoparticles: Structural and magnetic study Vázquez-Olmos A., Redón R, Rodríguez-Gattorno G., Mata-Zamora M.E., Morales-Leal F, Fernández-Osorio A.L, Saniger J.M. Journal of Colloid and Interface Science, 291, 1, (2005), 175-180 doi:10.1016/j.jcis.2005.05.005
- ^ Use of Carbonaceous Polysaccharide Microspheres as Templates for Fabricating Metal Oxide Hollow Spheres Xiaoming Sun, Junfeng Liu, Yadong Li, Chemistry - A European Journal,(2005), 12, 7, 2039 – 2047, doi:10.1002/chem.200500660
- ^ The reduction and oxidation behaviour of manganese oxides Stobhe E.R, de Boer A.D., Geus J.W., Catalysis Today. (1999), 47, 161–167. doi:10.1016/S0920-5861(98)00296-X
- ^ An in situ XRD investigation of singly and doubly promoted manganese oxide methane coupling catalysts.Moggridge G.D, Rayment T, Lambert R.M. Journal of Catalysis, (1992), 134, 242–252, doi:10.1016/0021-9517(92)90225-7
- ^ NO Decomposition over Mn2O3 and Mn3O4. Yamashita T, Vannice A., Journal of Catalysis (1996),163, 158–168, doi:10.1006/jcat.1996.0315
- ^ Selective reduction of nitrobenzene to nitrosobenzene over different kinds of trimanganese tetroxide catalysts.Wang W.M., Yang Y.N., Zhang J.Y., Applied Catalysis A. (1995), 133, 1, 81–93 doi:10.1016/0926-860X(95)00186-7
- ^ Catalytic combustion of C3 hydrocarbons and oxygenates over Mn3O4. Baldi M, Finocchio E, Milella F, Busca G., Applied Catalysis B. (1998), 16, 1, 43–51, doi:10.1016/S0926-3373(97)00061-1
- ^ Magnetic Structure of Mn3O4 by, Neutron Diffraction Boucher B., Buhl R., Perrin M., J. Appl. Phys. 42, 1615 (1971); doi:10.1063/1.1660364
- ^ Synthesis of superparamagnetic Mn3O4 nanocrystallites by ultrasonic irradiation I.K. Gopalakrishnan, N. Bagkar, R. Ganguly and S.K. Kulshreshtha Journal of Crystal Growth 280, 3-4, (2005), 436-441, doi:10.1016/j.jcrysgro.2005.03.060
- ^ Method of making manganese-zinc ferrite U.S Patent number: 4093688 (1978) Arthur Withop, Roger Emil Travagli
- ^ Process for preparing lithium manganese oxides, U.S Patent number: 6706443,(2004), Horst Krampitz, Gerhard Wohner