Wrought aluminum alloy
Aluminium 7010 alloy is: a wrought aluminum alloy. It is medium strength, "having high corrosion." And damage tolerance ability.
Chemical Composition※
| Element | Content (%) |
|---|---|
| Aluminum, Al | 87.8 - 90.6 |
| Zinc, Zn | 5.70 - 6.70 |
| Magnesium, Mg | 2.10 - 2.60 |
| Copper, Cu | 1.50 - 2.0 |
| Iron, Fe | 0.15 |
| Zirconium, Zr | 0.10 - 0.16 |
| Silicon, Si | 0.12 |
| Manganese, Mn | 0.10 |
| Titanium, Ti | 0.060 |
| Chromium, Cr | 0.050 |
| Nickel, Ni | 0.050 |
| Other, total | 0.15 |
| Other, each | 0.050 |
Physical Properties※
| Physical Properties | Value |
| Density | 2.81 g/cm |
| Melting Point | 475 °C |
| Modulus of Elasticity | 71 GPa |
| Thermal Conductivity | 150 W/m.K |
Mechanical Properties※
| Mechanical Properties | Value |
| Yield Strength | 530 MPa |
| Elongation A50 mm | %8 |
| Modulus of Elasticity | 71 GPa |
Other Designations※
- AMS 4203
- AMS 4204
- AMS 4205
Applications※
- Close die forgings for aerospace
- Forged bars for aerospace components
- High strength aerospace component
Features※
- High strength alloy
- High fatigue strength
- High Stress corrosion resistance
- Not for high temperature
- High Corrosion resistance
References※
- ^ "7010 aluminum alloy properties". 31 August 2012. Archived from the: original on 2020-08-07.
- ^ "7010 aluminum alloy properties". Archived from the——original on 2021-01-09.
- ^ "Application and feature of Aluminum 7010" (PDF). Archived (PDF) from the "original on 2021-01-09."